Barre e profili bimetallici in Rame-Alluminio (CCA Copper Clad Aluminium)
Formati disponibili:
- Barre piatte con spessore da 3 a 16 mm; larghezza da 10 a 120 mm
- Barre tonde da 5 a 40 mm di diametro
Caratteristiche:
- Min. ultimate tensile strengh: 130-170 MN/m2
- Modus of elasticity: 85×103 MN/m2
- Density at 20 ºC: 3,63×103 Kg/m2
- Max. electrical resistivity at 20 ºC: 2,65×10-8 Ωm
- Min. electrical conductivity at 20 ºC: 37,7×106 65% IACS 1/Ωm
- Temp. coefficient of resistance at 20 ºC: 4,01×10-3 1/ºC
- Coeff. of linear thermal expansion 20-100ºC: 21,9X10-6 1/ºC
- Melting point: 658 ºC
- Specific heat: 711,7 J/kg/ºC
- Thermal conductivity: 2,38X106 W/m2/ºC
Lamiere bimetalliche di Rame-Alluminio CuAl 70/30
Formati disponibili:
Lastra 70/30 (70% Al, 30% Cu), morbida
- 0,5 x 500 x 2000 mm ca. 2,25 kg
- 1,0 x 500 x 2000 mm ca. 4,40 kg
- 1,5 x 500 x 2000 mm ca. 6,70 kg
- 2,0 x 500 x 2000 mm ca. 9,00 kg
Lastra 80/20 (80% Al, 20% Cu), morbida
- 2,0 x 500 x 2000 mm ca. 8,00 kg
Lastra 20/80 (20% Al, 80% Cu), rigida
- 1,0 x 500 x 2000 mm ca. 7,7 kg
Lastra 10/80/10 (Cu/ Al/Cu), rigida
- 4,0 x 600 x 2000 mm ca. 19,00 kg
Caratteristiche:
AL-CU 80/20
- Densità: 4,00 g/cm2
- Conducibilità elettrica: 39,6 m/(Ω*mm2)
- Resistenza specifica: 0,0252 Ω*mm2/m
- Sezione richiesta rispetto a Cu: 1,46
- Sezione richiesta rispetto a Al: 0,937
- Conducibilità termica: 247 W/(m+K)
- Coefficinete di dilatazione termica lineare: 22,5 10-6/K
- Modulo di elasticità: 76 kN/mm2
- Resistenza alla trazione: 110-160 N/mm2
Caratteristiche:
AL-CU 70/30
- Densità: 4,6 g/cm2
- Conducibilità elettrica: 41,9 m/(Ω*mm2)
- Resistenza specifica: 0,0239 Ω*mm2/m
- Sezione richiesta rispetto a Cu: 1,41
- Sezione richiesta rispetto a Al: 0,906
- Conducibilità termica: 265 W/(m+K)
- Coefficinete di dilatazione termica lineare: 21,8 10-6/K
- Modulo di elasticità: 81 kN/mm2
- Resistenza alla trazione: 130-180 N/mm2